Low-Temperature Synthesis of TiC Coating on Diamond Surface by Thermal Explosion Reaction

被引：0
|
作者：
Liu, Jialin [1 ]
Liang, Baoyan [2 ]
Jiao, Mingli [2 ]
机构：
[1] Zhongyuan Univ Technol, Sch Mechatron Engn, Zhengzhou 450007, Henan, Peoples R China
[2] Zhongyuan Univ Technol, Mat & Chem Engn Sch, Zhengzhou 450007, Peoples R China
来源：
JOURNAL OF SUPERHARD MATERIALS | 2024年 / 46卷 / 02期
关键词：
TiC; coating; diamond; thermal explosion; INTERMETALLICS; FABRICATION; RESISTANCE; PARTICLES;
D O I：
10.3103/S1063457624020059
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A TiC coating was rapidly formed on the surface of diamond particles by thermal explosion reaction using Ti/Carbon black/PTFE/Diamond powders as raw material. XRD and SEM were used to analyze and observe the phase composition and microstructure of the coating. Results show that the phase composition of bonders was TiC, Ti, and TiF3 after thermal explosion reaction. The diamond surface obtained after the reaction can achieve good coating. Changing the diamond content in the raw material can regulate the phase composition of the coating. The coating on the diamond surface was mainly composed of TiC. When the diamond content in the raw materials was 20-40%, the coating was composed of TiC and TiF3. When the diamond content in the raw material was 60-80%, the coating was composed of TiC and Ti.
引用
收藏
页码：106 / 111
页数：6
相关论文
共 50 条
  • [1] Coating on the Surface of Diamond Particles by Thermal Explosion Reaction Method
    Qi Qiquan Li
    Baoyan Zhang
    Wangxi Liang
    Li Zhang
    Journal of Superhard Materials, 2022, 44 : 191 - 197
  • [2] Coating on the Surface of Diamond Particles by Thermal Explosion Reaction Method
    Qiquan Li
    Zhang, Qi
    Liang, Baoyan
    Zhang, Wangxi
    Yang, Li
    JOURNAL OF SUPERHARD MATERIALS, 2022, 44 (03) : 191 - 197
  • [3] Coating of diamond by thermal explosion reaction
    Liang, Baoyan
    Dai, Zhen
    Zhang, Qi
    Zhang, Wangxi
    Zhang, Ruijie
    Liu, Ying
    Zhang, Jizhou
    Yang, Li
    DIAMOND AND RELATED MATERIALS, 2021, 119
  • [4] Sputtering Coating on the Surface of Diamond Particles Using High Temperature Generated by Thermal Explosion Reaction
    Liang, Baoyan
    Luo, Yitong
    Zhang, Wangxi
    Zhang, Jizhou
    Jiao, Mingli
    JOURNAL OF SUPERHARD MATERIALS, 2024, 46 (03) : 197 - 203
  • [5] Low-temperature synthesis of nanocrystalline TiC
    Chernikova, E.S.
    Timofeeva, I.I.
    Uvarova, I.V.
    Bykov, A.I.
    Skorokhod, V.V.
    Smirnov, V.P.
    Xiaoxing Weixing Jisuanji Xitong/Mini-Micro Systems, 1998, 19 (12): : 32 - 38
  • [6] Low-temperature CVD of diamond and NEA surface of diamond
    Hiraki, A
    PHYSICS OF DIAMOND, 1997, 135 : 179 - 193
  • [7] LOW-TEMPERATURE SURFACE STABILIZATION OF A DIAMOND TOOL
    Shmatov, A. A.
    Smilovenko, O. O.
    SCIENCE & TECHNIQUE, 2009, (01): : 27 - 32
  • [8] SELECTIVE AND LOW-TEMPERATURE SYNTHESIS OF POLYCRYSTALLINE DIAMOND
    RAMESHAM, R
    ROPPEL, T
    ELLIS, C
    JAWORSKE, DA
    BAUGH, W
    JOURNAL OF MATERIALS RESEARCH, 1991, 6 (06) : 1278 - 1286
  • [9] UTILIZATION OF EXPLOSION REACTION FOR DIAMOND SYNTHESIS
    YAMAGUCHI, S
    SETAKA, N
    CARBON, 1979, 17 (04) : 371 - 372
  • [10] Titanium coating on the surface of diamond particles by a novel rapid low-temperature salt bath plating method
    Wei, Chenlong
    Xu, Xian
    Wei, Bangzheng
    Chen, Pengqi
    Cheng, Jigui
    CHEMICAL PHYSICS LETTERS, 2020, 761
12345