Mechanism for colouring hot-dip zinc alloy coating

被引：0
|
作者：
陈锦虹
卢锦堂
许乔瑜
曾广亮
李国雄
谢筠
机构：
[1] Guangzhou 510641
[2] China
[3] Department of Physics
[4] South China University of Technology
来源：
Science Bulletin | 1996年 / 06期
关键词：
coloured hot-dip zinc coating; interference of light through thin film; oxide film; ligand field;
D O I：
暂无
中图分类号：
TG174.44 [金属复层保护];
学科分类号：
080503 ;
摘要：
Hot-dip galvanizing is a widely used technique to prevent steel from oxidizing in air.However, only silver-grey zinc coating can no longer meet the need of people. At theWorld’s Fair in July 1989, Japanese first exhibited blue, red, yellow green andbrown hot-dip zinc coating sheets. These patent coatings are more incorruptible thantraditiona ones. This note tries to reveal the colouring mechanism of these coatings.
引用
收藏
页码：468 / 471
页数：4
相关论文
共 50 条
  • [1] Mechanism for colouring hot-dip zinc alloy coating
    Chen, JH
    Lu, JT
    Xu, QY
    Zeng, GL
    Li, GX
    Xie, J
    [J]. CHINESE SCIENCE BULLETIN, 1996, 41 (06): : 468 - 471
  • [2] Characteristics of hot-dip zinc coating measurement
    Bikulcius, G
    Rucinskiené, A
    Matulionis, E
    [J]. TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2003, 81 : 73 - 74
  • [3] GAS WIPING MECHANISM IN HOT-DIP COATING PROCESS
    TAKEISHI, Y
    YAMAUCHI, A
    MIYAUCHI, S
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1995, 81 (06): : 643 - 648
  • [4] THE PROBLEM WITH THE ZINC COATING DIVERSIFICATION OF THE HOT-DIP GALVANIZED STEEL
    Wegrzynkiewicz, Sylwia
    [J]. METAL 2015: 24TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2015, : 916 - 922
  • [5] THERMAL DIFFUSION AS THE ALTERNATIVE OF HOT-DIP ZINC COATING FOR FASTENERS
    Jedrzejczyk, Dariusz
    Szlapa, Ilona
    Skotnicki, Wojciech
    Was-Solipiwo, Joanna
    Jurasz, Zbigniew
    [J]. METAL 2017: 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2017, : 1059 - 1064
  • [6] Hot-dip zinc alloy coating with aluminum and magnesium protects steel sheet from corrosion
    Bertol, Art
    [J]. MATERIALS PERFORMANCE, 2013, 52 (02) : 15 - 16
  • [7] Kinds of defect and mechanism of formation on the hot-dip galvanized coating
    Kashiwaya, Yoshiaki
    Sato, Akira
    Ishii, Kunlyoshi
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2007, 71 (04) : 379 - 387
  • [8] The Mechanism of Dross Formation during Hot-dip Al-Zn Alloy Coating Process
    Luo, Qun
    Jin, Feng
    Li, Qian
    Zhang, Jie-Yu
    Chou, Kuo-Chih
    [J]. JOURNAL FOR MANUFACTURING SCIENCE AND PRODUCTION, 2013, 13 (1-2) : 85 - 89
  • [9] Effect of Ti and Al addition on microstructure of hot-dip zinc coating
    [J]. Wang, S.-M. (wsmkm2000@sina.com), 1600, Editorial Office of Transactions of Materials, 18 Xueqing Road, Beijing, 100083, China (34):
  • [10] Microstructure and properties of hot-dip PbSn alloy coating on copper wires
    Yao Xiao-fei
    Tian Wei
    Li Nan
    Wang Ping
    Lyu Yu-kun
    [J]. CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2020, 48 (03): : 148 - 154
12345