Effect of nodularity on mechanical properties and fracture of ferritic spheroidal graphite iron

被引：0

作者：

Zehua Wang ^{[1
]}

Xin Zhang ^{[1
]}

Feilong Xu ^{[1
]}

Kuncai Qian ^{[2
]}

Kaimin Chen ^{[2
]}

机构：

[1] College of Mechanics and Materials, Hohai University

[2] CRRC Qishuyan Institute Co,

来源：

ChinaFoundry | 2019年 / 16卷 / 06期

关键词：

D O I：

暂无

中图分类号：

TG143.5 [球墨铸铁];

学科分类号：

摘要：

Ferritic spheroidal graphite irons with nodularity from 72% to 96% were prepared. The relationship between the nodularity and the mechanical properties of the ferritic spheroidal graphite iron was investigated. The effect of nodularity on the mechanical properties and tensile fracture of the cast iron were studied. Results showed that the tensile strength Rm, yield strength Rp0.2, elongation to failure A5, and impact energy KV2 of the cast iron had a good linear relationship with its nodularity. Nodularity and annealing treatment would obviously affect the fracture characteristics of ferritic spheroidal graphite iron. The annealed ferritic spheroidal graphite iron with 93% nodularity showed a completely ductile rupture. With the decrease of nodularity from 93% to 72%, the cleavage fracture area ratio increased gradually from 0% to 8.3%. Compared with as-cast ferritic spheroidal graphite iron, annealing treatment reduced the cleavage fracture area of the ferritic spheroidal graphite iron.

引用

页码：386 / 392

页数：7

共 50 条

[1] Effect of nodularity on mechanical properties and fracture of ferritic spheroidal graphite iron
Wang, Ze-hua
Zhang, Xin
Xu, Fei-long
Qian, Kun-cai
Chen, Kai-min
CHINA FOUNDRY, 2019, 16 (06) : 386 - 392
[2] Effect of nodularity on mechanical properties and fracture of ferritic spheroidal graphite iron
Wang Z.-H.
Zhang X.
Xu F.-L.
Qian K.-C.
Chen K.-M.
China Foundry, 2019, 16 (6) : 386 - 392
[3] Effect of nodularity on mechanical properties and fracture of ferritic spheroidal graphite iron
Ze-hua Wang
Xin Zhang
Fei-long Xu
Kun-cai Qian
Kai-min Chen
China Foundry, 2019, (06) : 386 - 392
[4] Local approach of fracture in ferritic spheroidal graphite cast iron
GuillemerNeel, C
Beranger, AS
Clavel, M
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 843 - 848
[5] Effect of Preheat on Ferritic Spheroidal Graphite Cast Iron Joined by the Arc Welding on the Microstructure and Mechanical Properties
Yalcin, Necati
JOURNAL OF POLYTECHNIC-POLITEKNIK DERGISI, 2008, 11 (02): : 153 - 159
[6] Effect of Mo on Micro-structural and Mechanical Properties of As-Cast Ferritic Spheroidal Graphite Iron
Sumeet Chavan
Himanshu Khandelwal
Transactions of the Indian Institute of Metals, 2021, 74 : 2703 - 2711
[7] Effect of Mo on Micro-structural and Mechanical Properties of As-Cast Ferritic Spheroidal Graphite Iron
Chavan, Sumeet
Khandelwal, Himanshu
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2021, 74 (11) : 2703 - 2711
[8] Effect of microstructure on resonant vibration fatigue fracture of ferritic spheroidal graphite cast iron
Lin, SC
Lui, TS
Chen, LH
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2000, 13 (02) : 77 - 83
[9] Effect of a ferritization heat treatment on the fracture toughness of ferritic spheroidal graphite cast iron
Monchoux, JP
Verdu, C
Fougeres, R
SCRIPTA MATERIALIA, 2000, 42 (11) : 1047 - 1052
[10] Effect of triaxial stress on ductility and fracture morphology of ferritic spheroidal graphite cast iron
Lin, Y.F.
Lui, T.S.
Chen, L.H.
Metallurgical transactions. A, Physical metallurgy and materials science, 1994, 25 A (04): : 821 - 825

← 1 2 3 4 5 →