ON LOADING MODE (I, III) TECHNIQUE AS A MEANS OF DETERMINATION OF CRACK-GROWTH MECHANISM IN STRESS-CORROSION CRACKING

被引：0

|

作者：

MARICHEV, VA

机构：

来源：

WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION | 1989年 / 40卷 / 06期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

引用

收藏

页码：369 / 373

页数：5

相关论文

共 50 条

[1] ON LOADING MODE (I,III) TECHNIQUE AS A MEANS OF DETERMINATION OF CRACK GROWTH MECHANISM IN STRESS-CORROSION CRACKING.
Marichev, V.A.
Key Engineering Materials, 1987, 20-28 (pt 1-4)
[2] KINETICS AND MECHANISM OF CRACK-GROWTH DURING STRESS-CORROSION CRACKING OF ZIRCONIUM ALLOYS
KOMISSARENKO, LM
MARICHEV, VA
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1981, 32 (11): : 485 - 488
[3] SUBCRITICAL CRACK-GROWTH - FATIGUE, CREEP AND STRESS-CORROSION CRACKING
TOMKINS, B
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1981, 299 (1446): : 31 - 44
[4] THE MECHANISMS OF CRACK-GROWTH IN STRESS-CORROSION CRACKING OF ALUMINUM-ALLOYS
MARICHEV, VA
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1983, 34 (06): : 300 - 308
[5] MECHANISMS OF CRACK FORMATION AND CRACK-GROWTH IN CHLORIDE-INDUCED STRESS-CORROSION CRACKING
BEYER, C
SPECKHARDT, H
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 1989, 20 (03) : 69 - 72
[6] LOADING MODE AND STRESS-CORROSION CRACKING MECHANISMS
NICHOLS, FA
CORROSION, 1983, 39 (11) : 449 - 451
[7] THE THRESHOLD STRESS INTENSITY FOR STRESS-CORROSION CRACK-GROWTH
SMITH, E
RES MECHANICA, 1982, 4 (02): : 151 - 157
[8] FACTORS INFLUENCING STRESS-CORROSION CRACK-GROWTH KINETICS
PARKINS, RN
CORROSION, 1987, 43 (03) : 130 - 139
[9] RAPID STRESS-CORROSION CRACK-GROWTH IN IRRADIATED ZIRCALOY
PETTERSSON, K
JOURNAL OF NUCLEAR MATERIALS, 1982, 107 (01) : 117 - 121
[10] SYMPOSIUM ON CRACK-GROWTH BEHAVIOR AND PERFORMANCE OF STRUCTURAL COMPONENTS SUSCEPTIBLE TO STRESS-CORROSION CRACKING - INTRODUCTION
HORN, RM
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1986, 108 (01): : 1 - 1

← 1 2 3 4 5 →