Thermal Aging Behavior of H-NBR/NBR Blend

In the present investigation, thermal aging behavior of H-NBR/NBR blend with various H-NBR content was investigated. Mixture of dicumyl peroxide and sulfur were used as a curing agent. The influence of the thermal aging of the H-NBR/NBR blends on the solid state properties such as tensile strength, elongation at break, hardness and abrasion resistance was investigated. Tensile strength was increased with increasing H-NBR content, while abrasion resistance was decreased. Both elongation at break and hardness were not affected by the addition of H-NBR. The properties such as hardness, tensile strength and elongation at break of the aged samples were lower than unaged samples. However, the rate of deterioration of those properties was decreased by increasing the H-NBR content, which indicated that improved thermal aging behavior was obtained by the addition of H-NBR. Abrasion loss was increased with increasing aging time, but it became less by the addition of H-NBR addition.