NITRIDE CAPACITIES IN THE CAO-AL2O3 MELTS

被引：0
|
作者：
TOMIOKA, K
SUITO, H
机构：
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1992年 / 78卷 / 02期
关键词：
STEELMAKING; DENITROGENIZATION; NITRIDE CAPACITY; GAS-SLAG EQUILIBRIUM; CAO-AL2O3; SYSTEM; ZRO2 SOLID ELECTROLYTE;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The nitride capacities (C(N3) = (%N)P(O3)3/4/P(N2)1/2) in CaO-Al2O3 melts were measured by a gas-slag equilibration technique, using CaO, Al2O3, and Mo crucibles in the temperature range from 1 723 to 1 923 K. The oxygen partial pressures measured by a solid electrolyte cell were controlled by N2-H2-H2O gas mixtures. It was found that the nitride capacities increased with increasing temperature and Al2O3 content in slag. Activity coefficients of AlN increased with decrease of Al2O3 content and temperature.
引用
收藏
页码：260 / 266
页数：7
相关论文
共 50 条
  • [1] NITRIDE CAPACITY OF CAO-AL2O3 MELTS
    TOMIOKA, K
    SUITO, H
    ISIJ INTERNATIONAL, 1991, 31 (11) : 1316 - 1321
  • [2] Solubility of carbon in CaO-Al2O3 melts
    Kuwata, M
    Suito, H
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1996, 27 (01): : 57 - 64
  • [3] CARBURIZATION RATE OF CAO-AL2O3 MELTS
    SCHWERDTFEGER, K
    SCHUBERT, HG
    ARCHIV FUR DAS EISENHUTTENWESEN, 1974, 45 (08): : 499 - 507
  • [4] NITRIDE CAPACITIES IN CAO-SIO2 AND CAO-SIO2-AL2O3 MELTS
    TOMIOKA, K
    SUITO, H
    STEEL RESEARCH, 1992, 63 (01): : 1 - 6
  • [5] Molecular dynamics study of CaO-Al2O3 melts
    Belashchenko, DK
    Skvortsov, LV
    INORGANIC MATERIALS, 2001, 37 (05) : 476 - 481
  • [6] MICRO-NON-UNIFORMITY OF CAO-AL2O3 MELTS
    ZHMOYDIN, GI
    SMIRNOV, GS
    GLADKIY, VN
    RUSSIAN METALLURGY, 1976, (06): : 56 - 60
  • [7] Surface tension of CaO-Al2O3, CaO-SiO2, and CaO-Al2O3-SiO2 melts
    N. A. Arutyunyan
    A. I. Zaitsev
    N. G. Shaposhnikov
    Russian Journal of Physical Chemistry A, 2010, 84 : 7 - 12
  • [8] Surface Tension of CaO-Al2O3, CaO-SiO2, and CaO-Al2O3-SiO2 Melts
    Arutyunyan, N. A.
    Zaitsev, A. I.
    Shaposhnikov, N. G.
    RUSSIAN JOURNAL OF PHYSICAL CHEMISTRY A, 2010, 84 (01) : 7 - 12
  • [9] Nitride capacities of CaO-Al2O3-CaF2 melts at 1 773 K
    Shin, WY
    Lee, HG
    ISIJ INTERNATIONAL, 2001, 41 (03) : 239 - 246
  • [10] Activities of Aluminum and Calcium Oxides in the CaO-Al2O3 and CaO-SiO2-Al2O3 Melts
    Nevidimov, V. N.
    Durina, Yu M.
    Krasikov, S. A.
    Zhilina, E. M.
    Bykov, A. S.
    RUSSIAN METALLURGY, 2022, 2022 (02): : 134 - 141
12345