HOT ISOSTATIC PRESSING AND CHARACTERIZATION OF SOL-GEL-DERIVED CHROMIUM(III) OXIDE

被引：52
|
作者：
KAWABATA, A
YOSHINAKA, M
HIROTA, K
YAMAGUCHI, O
机构：
[1] Department of Molecular Science and Technology, Faculty of Engineering, Doshisha University, Tanabe, Kyoto
来源：
JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1995年 / 78卷 / 08期
关键词：
D O I：
10.1111/j.1151-2916.1995.tb08655.x
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Chromium(III) oxide (Cr2O3) crystallizes at low temperatures from an amorphous material prepared by adding hydrazine monohydrate to an aqueous solution of Cr(NO3)(3). 9H(2)O. Individual particles of Cr2O3 tend toward a hexago nal morphology above 800 degrees C. Well-densified Cr2O3 pellets (98.8% of theoretical density) have been fabricated by hot isostatic pressing for 2 h at 1100 degrees C and 196 MPa. Their fracture toughness is 4.4 MPa . m(1/2). The sample annealed in air for 12 h at 1300 degrees C exhibits a high electrical conductivity of 3.6 Ohm-1.m(-1) at 700 degrees C.
引用
收藏
页码：2271 / 2273
页数：3
相关论文
共 50 条
  • [1] Hot isostatic pressing and characterization of sol-gel-derived chromium(III) oxide
    1600, American Ceramic Soc, Westerville, OH, USA (78):
  • [2] Densification of sol-gel-derived mullite ceramics after cold isostatic pressing up to 1 GPa
    Kamiya, Hidehiro
    Suzuki, Hisao
    Ichikawa, Takahiro
    Cho, Yong Ick
    Horio, Masayuki
    1998, American Ceramic Soc, Westerville, OH, United States (81)
  • [3] Densification of sol-gel-derived mullite ceramics after cold isostatic pressing up to 1 GPa
    Kamiya, H
    Suzuki, H
    Ichikawa, T
    Cho, YI
    Horio, M
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1998, 81 (01) : 173 - 179
  • [4] Characterization of sol-gel-derived cobalt oxide xerogels as electrochemical capacitors
    Lin, C
    Ritter, JA
    Popov, BN
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (12) : 4097 - 4103
  • [5] Characterization of sol-gel-derived silica films
    J Non Cryst Solids, 1-2 (72):
  • [6] Synthesis and Characterization of Sol-Gel-Derived Chemical Mullite
    Roy, J.
    Maitra, S.
    JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2014, 5 (01): : 57 - 61
  • [7] Characterization of sol-gel-derived NiOx xerogels as supercapacitors
    Cheng, Jie
    Cao, Gao-Ping
    Yang, Yu-Sheng
    JOURNAL OF POWER SOURCES, 2006, 159 (01) : 734 - 741
  • [8] Spectroscopic characterization of sol-gel-derived mixed oxides
    Miller, JM
    Lakshmi, LJ
    JOURNAL OF PHYSICAL CHEMISTRY B, 1998, 102 (34): : 6465 - 6470
  • [9] Fabrication and characterization of sol-gel-derived zinc oxide thin-film transistor
    Hwang, Young Hwan
    Seo, Seok-Jun
    Bae, Byeong-Soo
    JOURNAL OF MATERIALS RESEARCH, 2010, 25 (04) : 695 - 700
  • [10] Fabrication and characterization of sol-gel-derived zinc oxide thin-film transistor
    Young Hwan Hwang
    Seok-Jun Seo
    Byeong-Soo Bae
    Journal of Materials Research, 2010, 25 : 695 - 700
12345