THE STRENGTH OF PITCH-BASED CARBON-FIBER AT HIGH-TEMPERATURE

被引：19
|
作者：
TANABE, Y
YASUDA, E
BUNSELL, AR
FAVRY, Y
INAGAKI, M
SAKAI, M
机构：
[1] ECOLE NATL SUPER MINES,CTR MAT,F-91003 EVRY,FRANCE
[2] TOYOHASHI UNIV TECHNOL,TOYOHASHI,AICHI 440,JAPAN
来源：
JOURNAL OF MATERIALS SCIENCE | 1991年 / 26卷 / 06期
关键词：
D O I：
10.1007/BF00544669
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The strengths of some high modulus pitch-based carbon fibres have been determined up to 1300-degrees-C in both air and nitrogen atmospheres. The fibres possessed Young's moduli of 700 GPa and were 10-mu-m in diameter. The strength of the fibres was seen to be gauge length dependent but to a lesser extent than is usual with PAN-based carbon fibres. The fibre strength was observed to increase with temperature as did the Weibull modulus.
引用
收藏
页码：1601 / 1604
页数：4
相关论文
共 50 条
  • [1] PROGRESS OF PITCH-BASED CARBON-FIBER IN JAPAN
    OTANI, S
    OYA, A
    [J]. ACS SYMPOSIUM SERIES, 1986, 303 : 323 - 334
  • [2] SOME FACTORS FOR THE HIGH PERFORMANCES OF MESOPHASE PITCH-BASED CARBON-FIBER
    MOCHIDA, I
    LING, LC
    KORAI, Y
    [J]. JOURNAL OF MATERIALS SCIENCE, 1994, 29 (11) : 3050 - 3056
  • [3] PREPARATION OF PITCH-BASED ANTIBACTERIAL ACTIVATED CARBON-FIBER
    OYA, A
    WAKAHARA, T
    YOSHIDA, S
    [J]. CARBON, 1993, 31 (08) : 1243 - 1247
  • [4] PLEAT STRUCTURE OF THE MESOPHASE PITCH-BASED CARBON-FIBER
    YOON, SH
    KORAI, Y
    MOCHIDA, I
    [J]. CARBON, 1994, 32 (06) : 1182 - 1186
  • [5] MESOPHASE PITCH-BASED CARBON-FIBER PRODUCTION PROGRAM
    HAGER, DS
    SCHMIDT, DL
    [J]. TOMORROWS MATERIALS : TODAY, BOOK 1 AND 2: 34TH INTERNATIONAL SAMPE SYMPOSIUM AND EXHIBITION, 1989, 34 : 178 - 189
  • [6] BEARING STRENGTH AND DAMAGE PROGRESS FOR PAN-BASED AND PITCH-BASED CARBON-FIBER COMPOSITES
    MAIKUMA, H
    KUBOMURA, K
    [J]. JOURNAL OF COMPOSITE MATERIALS, 1993, 27 (18) : 1739 - 1761
  • [7] WATER-TREATMENT BY PITCH-BASED ACTIVATED CARBON-FIBER
    SHINDO, N
    OTANI, Y
    INOUE, G
    KAWAZOE, K
    [J]. DESALINATION, 1994, 98 (1-3) : 155 - 160
  • [8] EFFECT OF SPINNING CONDITIONS ON STRUCTURES OF PITCH-BASED CARBON-FIBER
    MATSUMOTO, M
    IWASHITA, T
    ARAI, Y
    TOMIOKA, T
    [J]. CARBON, 1993, 31 (05) : 715 - 720
  • [9] Pitch-based carbon fiber with improved compressive strength
    Furuyama, M
    Arai, Y
    Katoh, O
    Harakawa, M
    [J]. EVOLVING TECHNOLOGIES FOR THE COMPETITIVE EDGE, BOOKS 1 AND 2, 1997, 42 : 738 - 744
  • [10] Fractal structure change of pitch-based carbon fiber during high-temperature heat treatment
    Xiao, Peng
    Zhang, Shujiao
    Gong, Yanjun
    Liu, Yue
    Li, Zhihong
    Li, Dongfeng
    [J]. CHEMICAL PHYSICS LETTERS, 2023, 811
12345