MELT PROCESSING OF THE Bi2Sr2CaCu2Oy SUPERCONDUCTOR IN OXYGEN AND ARGON ATMOSPHERES

被引：7
|
作者：
Holesinger, T. G. [1 ]
Miller, D. J. [1 ]
Chumbley, L. S.
机构：
[1] Argonne Natl Lab, Div Mat Sci, 9700 S Cass Ave, Argonne, IL 60439 USA
来源：
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 1993年 / 3卷 / 01期
基金：
美国国家科学基金会;
关键词：
D O I：
10.1109/77.233342
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Solidification and subsequent annealing of Bi2Sr2CaCu2Oy (2212) in oxygen and argon atmospheres were investigated in order to identify alternative processing routes for controlling microstructures and superconducting properties. In addition to 2212, several other phases formed on cooling in O-2 and did not disappear upon subsequent annealing. Crystallization in Ar resulted in a divorced eutetic structure of Bi2Sr3-xCaxOy and Cu2O/CuO. The superconductor was formed on subsequent anneals. Samples melted in Ar and then annealed generally possessed a more uniform microstructure compared with samples that were melted in oxygen and annealed. Compositional measurements of the 2212 phase suggest that CaO segregation in the melt may be minimized with an overall composition such as Bi2.15Sr2Ca0.85Cu2Oy
引用
收藏
页码：1178 / 1181
页数：4
相关论文
共 50 条
  • [1] Isothermal melt processing of Bi2Sr2CaCu2Oy round wire
    Holesinger, T.G., 1600, Elsevier Science B.V., Amsterdam, Netherlands (253): : 1 - 2
  • [2] POTASSIUM SUBSTITUTION IN THE BI2SR2CACU2OY SUPERCONDUCTOR
    KRISHNA, BG
    CHANDRA, GR
    SURYANARAYANA, SV
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1994, 25 (2-3): : 153 - 158
  • [3] Potassium substitution in the Bi2Sr2CaCu2Oy superconductor
    Krishna, B.Gopala
    Chandra, G.Ravi
    Suryanarayana, S.V.
    Materials science & engineering. B, Solid-state materials for advanced technology, 1994, B25 (2-3): : 153 - 158
  • [4] SOLID-SOLUTION REGION OF THE BI2SR2CACU2OY SUPERCONDUCTOR
    HOLESINGER, TG
    MILLER, DJ
    CHUMBLEY, LS
    PHYSICA C, 1993, 217 (1-2): : 85 - 96
  • [5] EFFECTS OF COOLING RATE ON THE PROPERTIES AND THE OXYGEN-CONTENT OF THE SUPERCONDUCTOR BI2SR2CACU2OY
    ZHENG, FC
    JIANG, JY
    SUN, YP
    YIN, HQ
    DU, JJ
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1989, 115 (01): : K75 - K78
  • [6] Phase decomposition and oxygen diffusion of Bi2Sr2CaCu2Oy single crystals annealed in various atmospheres
    Sun, XF
    Wu, WB
    Zhao, XR
    Zheng, L
    Zhou, G
    Li, XG
    Zhang, YH
    PHYSICA C, 1997, 279 (1-2): : 47 - 50
  • [7] Al2O3 additions for isothermal melt processing of Bi2Sr2CaCu2Oy
    Holesinger, TG
    JOURNAL OF MATERIALS RESEARCH, 1996, 11 (09) : 2135 - 2141
  • [8] Conduction noise in Bi2Sr2CaCu2Oy
    Togawa, Y
    Abiru, R
    Iwaya, K
    Kitano, H
    Maeda, A
    PHYSICA C, 2000, 341 : 1215 - 1216
  • [9] Ag injection to Bi2Sr2CaCu2Oy superconductor by shock-loading
    Kikuchi, M
    Tsukagoshi, K
    Atou, T
    Ohshima, E
    Faqir, H
    Fukuoka, K
    Nojima, T
    Itou, S
    Watanabe, K
    Syono, Y
    JOURNAL DE PHYSIQUE IV, 2005, 123 : 145 - 149
  • [10] Influence of the initial conditions on crystal growth of the Bi2Sr2CaCu2Oy superconductor
    Faqir, H
    Monnereau, O
    Badeche, T
    Vacquier, G
    Casalot, A
    JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1997, 58 (05) : 821 - 827
12345