INSITU OBSERVATION OF CASCADE DAMAGE UNDER HEAVY-ION IRRADIATION

被引：4

作者：

SEKIMURA, N ^{[1
]}

ISHINO, S ^{[1
]}

机构：

[1] UNIV TOKYO,DEPT NUCL ENGN,BUNKYO KU,TOKYO 113,JAPAN

来源：

RADIATION EFFECTS AND DEFECTS IN SOLIDS | 1992年 / 124卷 / 01期

关键词：

CASCADE DAMAGE; HEAVY ION IRRADIATION; INSITU OBSERVATION; GOLD; NICKEL; LIFETIME OF DEFECT CLUSTERS; POINT-DEFECT BURST;

D O I：

10.1080/10420159208219832

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

Collision cascades initiated from high energy PKAs produce defect clusters in crystalline solids irradiated with fast neutrons or energetic ions. They will affect not only an early stage of microstructuraI evolution but that at high fluence by changing free defect survival rate. To elucidate fundamental processes of cascade damage evolution, in situ observation of microstructure in FCC metals under heavy ion irradiation has been carried out using a combined facility of a 400 kV accelerator and a 200 kV transmission electron microscope installed in the University of Tokyo, Tokai. Defect clusters produced by individual energetic ions are observed during irradiation to examine subcascade formation, interaction of point-defects from cascade damage and related point-defect processes. © 1992, Taylor & Francis Group, LLC. All rights reserved.

引用

页码：109 / 116

页数：8

共 50 条

[1] INSITU OBSERVATION OF CASCADE DAMAGE IN NICKEL AND COPPER UNDER HEAVY-ION IRRADIATION
SAKAIDA, H
SEKIMURA, N
ISHINO, S
[J]. JOURNAL OF NUCLEAR MATERIALS, 1991, 179 : 928 - 930
[2] INSITU OBSERVATION OF CASCADE DAMAGE IN GOLD UNDER HEAVY-ION IRRADIATION AT HIGH-TEMPERATURE
ISHINO, S
SEKIMURA, N
HIROOKA, K
MUROGA, T
[J]. JOURNAL OF NUCLEAR MATERIALS, 1986, 141 : 776 - 780
[3] ACCUMULATION PROCESSES OF CASCADE DAMAGE UNDER HEAVY-ION IRRADIATION
KANZAKI, Y
SEKIMURA, N
ISHINO, S
[J]. JOURNAL OF NUCLEAR MATERIALS, 1992, 191 : 1119 - 1122
[4] DIRECT OBSERVATION OF CASCADE DEFECTS BY INSITU HEAVY-ION ELECTRON-MICROSCOPE INTERFACE
ISHINO, S
[J]. RADIATION EFFECTS AND DEFECTS IN SOLIDS, 1990, 113 (1-3): : 29 - 37
[5] STABILITY OF CASCADE CLUSTERS IN GOLD UNDER ENERGETIC HEAVY-ION IRRADIATION
SEKIMURA, N
ISHINO, S
[J]. JOURNAL OF NUCLEAR MATERIALS, 1988, 155 : 1217 - 1221
[6] ANNEALING OF HEAVY-ION CASCADE DAMAGE IN SILICON
THOMPSON, DA
GOLANSKI, A
HAUGEN, HK
HOWE, LM
DAVIES, JA
[J]. RADIATION EFFECTS LETTERS, 1980, 50 (3-6): : 125 - 131
[7] CASCADE DAMAGE IN MOLYBDENUM AND NICKEL BY HEAVY-ION IRRADIATION WITH ENERGIES AROUND 100 MEV
SASAKI, S
IWASE, A
KAZUMATA, Y
IWATA, T
[J]. JOURNAL OF NUCLEAR MATERIALS, 1988, 155 : 1192 - 1195
[8] INSITU OBSERVATIONS OF HEAVY-ION DAMAGE IN STAINLESS-STEEL
FUKUYA, K
KAWANISHI, H
ISHINO, S
[J]. JOURNAL OF NUCLEAR MATERIALS, 1982, 103 (1-3) : 1385 - 1389
[9] HEAVY-ION IRRADIATION DAMAGE IN CARBON STRIPPER FOILS
DOLLINGER, G
MAIERKOMOR, P
[J]. NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION A-ACCELERATORS SPECTROMETERS DETECTORS AND ASSOCIATED EQUIPMENT, 1989, 282 (01): : 223 - 235
[10] PRECIPITATION KINETICS UNDER HEAVY-ION IRRADIATION IN CUBE
KOCH, R
[J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1985, 51 (03): : L19 - L22

← 1 2 3 4 5 →