ORIGIN OF COERCIVITY IN (FE,CO)-BASED GRANULAR FILMS

被引：28
|
作者：
TSOUKATOS, A [1 ]
WAN, H [1 ]
HADJIPANAYIS, GC [1 ]
PAPAEFTHYMIOU, V [1 ]
KOSTIKAS, A [1 ]
SIMOPOULOS, A [1 ]
机构：
[1] DEMOKRITOS NRC,INST MAT SCI,GR-60228 ATHENS,GREECE
来源：
JOURNAL OF APPLIED PHYSICS | 1993年 / 73卷 / 10期
关键词：
D O I：
10.1063/1.352399
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The magnetic behavior of Co and Fe granular films was studied relative to their host matrix environment (BN, SiO2). The crystal structure of Co and Fe in the as-deposited samples is alpha-Co (hcp) and alpha-Fe (bcc) respectively, with particle sizes ranging between 3 and 9 nm. The coercivities measured ranged from a few tens to a few hundreds Oe, with the higher values observed for particles embedded in the oxygen based matrix.
引用
收藏
页码：6967 / 6969
页数：3
相关论文
共 50 条
  • [1] Origin of coercivity in (Fe,Co)-based granular films
    Tsoukatos, A.
    Wan, H.
    Hadjipanayis, G.C.
    Papaefthymiou, V.
    Kostikas, A.
    Simopoulos, A.
    1600, (73):
  • [2] ORIGIN OF COERCIVITY IN A CR-CO-FE ALLOY (CHROMINDUR)
    MAHAJAN, S
    GYORGY, EM
    SHERWOOD, RC
    JIN, S
    NAKAHARA, S
    BRASEN, D
    EIBSCHUTZ, M
    APPLIED PHYSICS LETTERS, 1978, 32 (10) : 688 - 690
  • [3] High coercivity and perpendicular anisotropy in Co-Cu granular films
    Tuan, NA
    Luong, NH
    Chau, N
    Van Hiep, V
    Ha, NM
    PHYSICA B-CONDENSED MATTER, 2003, 327 (2-4) : 400 - 403
  • [4] CRITICAL THICKNESS AND COERCIVITY OF CO-NI-FE FILMS
    GORRES, JM
    HANSON, MM
    APPLIED PHYSICS LETTERS, 1968, 12 (04) : 146 - &
  • [5] ORIGIN OF ENHANCED COERCIVITY IN (FE65CO35)X(AL2O3)1-X GRANULAR THIN-FILMS
    HSU, JH
    CHANG, CR
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1993, 120 (1-3) : 342 - 344
  • [6] COERCIVITY OF CO-FE-P THIN FERROMAGNETIC-FILMS
    BURSUC, ID
    DIACONU, E
    THIN SOLID FILMS, 1977, 46 (01) : 1 - 6
  • [7] Coercivity mechanism of nanocomposite Sm-Co/Fe multilayer films
    Zhang, Jian
    Li, Yang-xian
    Wang, Fang
    Shen, Bao-gen
    Sun, Ji-rong
    JOURNAL OF APPLIED PHYSICS, 2010, 107 (04)
  • [8] INHOMOGENEOUS CR CONCENTRATION AS ORIGIN OF THE PERPENDICULAR COERCIVITY IN CO-CR FILMS
    ANDRA, W
    DANAN, H
    IEEE TRANSACTIONS ON MAGNETICS, 1987, 23 (01) : 62 - 64
  • [9] Difference in coercivity between Co/Fe and Fe/Co bilayers
    Park, MH
    Hong, YK
    Gee, SH
    Mottern, ML
    Jang, TW
    Burkett, S
    JOURNAL OF APPLIED PHYSICS, 2002, 91 (10) : 7218 - 7220
  • [10] High coercivity Fe-Cr-Co thin films by vacuum evaporation
    Chin, Tsung-Shune, 1692, (30):
12345